FLAX
Dry Flax Fabrics Range
PRODUCT APPLICATIONS
LINCORE® FF is a 100% flax fabric made of untwisted rovings.
The moulding can be realized by :
Infusion, Resin Transfer Molding, Resin Film Infusion Lay up
These fabrics are also availble as resin-impregnated reinforcements for high strength, toughness ans structural performance at low weight.
PRODUCT APPLICATIONS
LINCORE® FF is mainly used for the following applications :
Automotive, Marine, Trucks, Sports & Leisure, Building, Urban & Industrial Parts, Energy.
COMPOSITE MECHANICAL CHARACTERISTICS
(After moulding with epoxy matrix and tested at ambient temperature)
|
Style
|
Standard with (mm)
|
Weave
|
Roving (Tex)
|
Weight (gr/m2)
|
SColour Warp/Weft
|
Appearence
|
| LINCORE® FF | 1000 / 1500 | Plain 1/1, Plain 2/2, Twill 2/2, 0° UD ou and 90° UD | 200 / 1000 | 153 to 750 | Natural |
|
|
FEATURES
|
PRODUCT BENEFITS
|
| WEIGHT SAVING | MECHANICAL PROPERTIES |
| GREEN MATERIAL | EASE OF STORAGE CONDITIONS |
| MOULDED WITH STANDARD PROCESSES | RECYCLABLILITY |
| THERMAL AND ACOUSTIC INSULATION | DRAPABILITY |
|
| Plain 1/1 LINCORE® FF P1 400 | UD 0° LINCORE® FF UD 250 | |||||
| Flax fibre | Type | Long | Long | ||||
| TENSILE | Strength | ISO 527 | MPa | 115 | +/- 3 | 270 | +/- 5 |
| Modulus
| GPa | 16.2 | +/- 1.5 | 28 | +/- 1 | ||
| Elongation
| % | 1.6 | +/- 0.2 | 1.4 | +/- 0.2 | ||
| FLEXURAL | Strength | ISO 14125 | MPa | 130 | +/- 8 | 226 | +/- 5 |
| Modulus
| GPa | 11.2 | +/- 0.8 | 25.7 | +/- 1.5 | ||
| FLAX content | In weight | % | 40 | 40 | |||
IDENTIFICATION
Example : LINCORE® FF P1 250 100
| FF : Flax Fabrics | P2 : Plain 2/2 | 250 : Nominal Weight (g/m2) |
| P1 : Plain 1/1 | T2 : Twill 2/2 | 100 : Standard width (cm) |
|
| UD : Unidirectionnal |
|